ALLOY718 (Inconel718)

Characteristics

ALLOY718 is a precipitation-hardenable Ni-Cr-Fe alloy containing significant amounts of Nb & Mo as well as lesser amounts of Al+Ti. The alloy has good ductility in the annealed condition and high strength up to 700 °C (1300 °F).

  • • good fabrication characteristics in the annealed condition
  • • good tensile, fatigue and creep-rupture strengths
  • • high-temperature strength up to 700 °C (1300°F)
  • • good oxidation resistance up to 1000°C (1830°F)
  • • excellent mechanical properties in cryogenic environments
  • • excellent corrosion resistance at high and low temperatures and good resistance to stress-corrosion cracking and pitting corrosion
  • • good weldability by arc and resistance welding processes without susceptibility to post-weld cracking
Density8.19

Stock Form and Sizes

※ ◆1000㎜ ◎2000㎜ ▲3000㎜ ■3500㎜ ●4000㎜ ★2500㎜~3990㎜

ALLOY 718ST Round barsSpecification:Round bars
(ST:Solution Annealed) AMS5662
ST/AG Common Standard:ASTM B637 ASME SB637 ※GE C50TF13(Chemical composition only) ※GE
B50T69(Chemical composition only) ※GE B50TF15 A&D(Chemical composition only) GE S-1000 GE S-400

★/▲ALLOY718 ST ☆ALLOY718 AG

size 1〜13
1.21.622.633.544.455.367.188.95101213
            
size 16〜50
1618192022242528303235363840424550
   
size 55〜135
556065707580859095100105110115120125130135
   
size 140〜300
140145150160165170180190200210220230250280300  
     
ALLOY 718AG Round barsSpecification:Round bars
(AG:Age Hardened) AMS5663
ST/AG Common Standard:ASTM B637 ASME SB637 ※GE C50TF13(Chemical composition only) ※GE
B50T69(Chemical composition only) ※GE B50TF15 A&D(Chemical composition only) GE S-1000 GE S-400

★/▲ALLOY718 ST ☆ALLOY718 AG

size 1〜13
1.21.622.633.544.455.367.188.95101213
             

size 16〜50
1618192022242528303235363840424550
    
size 55〜135
556065707580859095100105110115120125130135

101.6
    
size 140〜300
140145150160165170180190200210220230250280300  
  
 
 

  

Contact us

Sourceable Ex-Stock Material for other Forms from Distributors World-Wide

EquivalentRound BarsPlates/SheetsPipe/TubeWelding Rod & Wire
MinMaxMinMax
Inconel718 ST
Round bars(ASTM B637/AMS5662)
Plate(ASTM B670/AMS5596)
6.35〜3050.25〜101.6 
EquivalentRound BarsPlates/SheetsPipe/TubeWelding Rod & Wire
MinMaxMinMax
Inconel718 AG
(API6A/NACE)
12.7〜350   
EquivalentRound BarsPlates/SheetsPipe/TubeWelding Rod & Wire
MinMaxMinMax
Inconel718 AG
(ASTM B637/AMS5663)
4.75〜203.2   

*○: Various sizes available in stock. △: Only limited sizes available in stock. ☆: Please contact us for more details.
* We can supply materials and products that comply with various standards including ASTM, ASME, AMS, and NACE standards. Please contact us for more details.

Contact us

Corrosion resistance

The high chromium and molybdenum contents of Alloy 718 impart excellent resistance to uniform and localized corrosion, such as pitting in many media at both high and low temperatures. The chromium also enables it to withstand chloride-ion stress-corrosion cracking which makes it an excellent alloy for service in oil and sour gas (H2S containing) environments as well as seawater.
Alloy 718 is generally only used for applications not exceeding 700 °C (1300 °F). However, oxidation resistance up to 1000 °C (1830 °F) is particularly high and comparable to that of other gamma-prime (γ’) strengthened superalloys

Applications

Due to its high-temperature strength up to 700 °C (1300 °F), excellent corrosion resistance and ease of fabrication ALLOY718 finds applications in many fields. Initially it was used as a turbine disk material in aircraft jet engines. Here resistance to creep and stress rupture was most important.
Because of its properties, fabricability and cost effectiveness it has since gained wider acceptance. To-day applications vary from highly stressed rotating and static components in gas turbines and rocket engines to high-strength bolting, springs and fasteners, components in nuclear reactors and space vehicles as well as high-temperature tooling for extrusion, of for example copper, and shearing. Another more recent important application involves pump shafts and other highly stressed well head and downhole components in offshore and marine engineering. Particularly useful is the alloy for drilling equipment in sour (containing H2S, CO2 and chlorides) oil and gas wells.

Contact us

Chemical composition

 NiCrFeCMnSiCuMoCoNbAlTiB
min50.017.0bal.    2.80 4.750.200.65 
max55.021.00.080.350.350.303.301.05.500.801.150.006
 PSPbSeBiTa
min     0.05
max0.0150.0155ppm3ppm0.3ppm

※The values in the table are for reference only and do not guarantee minimum or maximum values. For further information, please contact us.

Mechanical properties(Round Bar)

 Yield Strength(Mpa) Tensile Strength(Mpa)Elongation(%)Reduction of Area(%)Hardness(HB)
ASTM Min Value103412751215331
Typical Values at RT1176134317 382

Above standard values and typical values of Round Bar.
Please contact us with any questions about reference or value of plate and pipe.
※Grade 1
※The values in the table are for reference only and do not guarantee minimum or maximum values. For further information, please contact us.

International Standard Comparison Chart

 MaterialRound BarsPlates/SheetsPipe/Tube
SeamlessWelded
ASTMUNS
N07718
B673B670  
ASMESB673SB670  
JISNCF718H4553G4901H4552 
DIN2.4668177521775017751 

Contact us

Disclaimer
All the information on this website is published in good faith and for general information purpose only and not for technical design purposes. We do not make any warranties about the completeness, reliability and accuracy of this information. Any action you take upon the information on our website is strictly at your own risk. and we will not be liable for any losses and damages in connection with the use of our website.

Stock list

CONTACT

OSAKA STAINLESS

Inquiry/Request for information

TEL 81-6-6586-5626
FAX 81-6-6586-5858

E-MAIL:info@osc21.co.jp

Business hours: 8:00 - 17:00(closed on Saturdays, Sundays and National Holidays)

Contact us